Abstract

Herein, a dual-functioning deep eutectic solvent system based on triethylmethylammonium chloride and imidazole was harnessed as a swelling agent and a reaction medium for the esterification of cellulose with n-octyl succinic anhydride (OSA). The modified or amphiphilic cellulose nanofibers (ACNFs), synthesized using three different OSA-to-anhydroglucose unit molar ratios (0.5:1, ACNF-1; 1:1, ACNF-2; and 1.5:1, ACNF-3), were further converted into nanofibers with degree of substitution (DS) values of 0.24–0.66. The ACNFs possessed a lateral dimension of 4.24–9.22 nm and displayed surface activity due to the balance of hydrophobic and hydrophilic characteristics. The ACNFs made stable aqueous dispersions; however, the instability index of ACNF-3 (0.51) was higher than those of ACNF-1 (0.29) and ACNF-2 (0.33), which was attributed to the high DS-induced hydrophobicity, causing the instability in water. The amphiphilic nature of ACNFs promoted their performance as stabilizers in oil-in-water Pickering emulsions with average droplet sizes of 4.85 μm (ACNF-1) and 5.48 μm (ACNF-2). Self-standing films of ACNFs showed high contact angles for all the tested DS variants (97.48–114.12°), while their tensile strength was inversely related to DS values (ACNF-1: 115 MPa and ACNF-3: 49.5 MPa). Aqueous dispersions of ACNFs were also tested for coating fruits to increase their shelf life. Coatings improved their shelf life by decreasing oxygen contact and moisture loss.